NM-Carbomer 990
Carbomer 990/NM-Carbomer 990 is a cross-linked polyacrylate polymer, polymerized in co-solvent system of ethyl acetate and cyclohexane. It is capable of providing high viscosity, excellent thickening and suspending performance with low-dosage. Its short flow (non-drip) properties are ideal for applications such as clear gels, hydroalcoholic gels, creams. When neutralized by alkali it forms sparkling clear water or hydroalcoholic gels and creams.
Carbomer 990/NM-Carbomer 990 is a cross-linked polyacrylate polymer, polymerized in co-solvent system of ethyl acetate and cyclohexane. It is capable of providing high viscosity, excellent thickening and suspending performance with low-dosage. Its short flow (non-drip) properties are ideal for applications such as clear gels, hydroalcoholic gels, creams. When neutralized by alkali it forms sparkling clear water or hydroalcoholic gels and creams.
Details:
Product name: NM-Carbomer 990
INCI: Carbomer
Appearance: White powder
Viscosity (0.5 wt% at pH 7): 45,000-70,000 mPa·s
Clarity: Above 95% transmittance in a 0.5 wt% gel
Typical use level: 0.2-1.0 wt%
Packaging: 20 kg per carton with PE liner
Product name: NM-Carbomer 990
INCI: Carbomer
Appearance: White powder
Viscosity (0.5 wt% at pH 7): 45,000-70,000 mPa·s
Clarity: Above 95% transmittance in a 0.5 wt% gel
Typical use level: 0.2-1.0 wt%
Packaging: 20 kg per carton with PE liner
Features and Benefits
l Short flow properties
l High viscosity
l High suspending, thickening and stabilizing ability
l High clarity
Recommended Applications
l Hair styling gels & Moisturizing gels
l Bath gels
l Hand, body and face lotions
l Creams
Formula Guidelines
l Typical recommended dosage at 0.2~1.0 wt %.
l To disperse NM-Carbomer940 completely, it should be slowly and carefully sprinkled to dispersion medium while the mix is stirred rapidly to avoid formation of lumps; extremely high shear rate mixer should be carefully employed to avoid viscosity loss.
l The ideal viscosity can be achieved at pH ranges of 5.0~10.0 when neutralized; In a hydoalcoholic system, a correct neutralizer must be chosen carefully based on the amount of alcohol to be gelled.
l After neutralization, high-shear and lasting stirring should be avoided to keep stable thickening ability.